Lead-acid battery is a farm trucks and tractors an important component of the electrical system. Battery life with the use of maintenance is closely related to the use of improper maintenance will cause early damage to batteries Inspiron E1405 battery , Inspiron E1505 battery . Therefore, a careful use of good battery maintenance is very necessary. In addition, the battery sometimes in the course of some damage, the user to take some temporary measures, real-time to repair, to avoid adversely affected by farming season and reduce losses.
First, the use of lead-acid battery maintenance
1, the correct installation Datie pole piles. The present agricultural vehicles and tractors on the generator with the rectifier is equipped with the battery negative Datie, and DC generator with laptop battery is used in cathode Datie, can not hold against; otherwise the former will burn silicon diode, which will burn regulator contact. Lead-acid battery pole pile marked “+” sign is positive, marked “-” number is negative. No tags, you can identify by the following characteristics: a very thick pile is positive, smaller is the negative; great pile on the oxide is more positive, less is negative; very dark brown pile is positive, pale gray is negative; also available from the poles leads to a pile on each wire, 1K500 battery , 1X793 battery inserted in the same acid in the cup, there are a large number of bubbles produced is negative.
2, do not make excessive battery discharge. Use electric starter starts, each operation shall not exceed 5s; the first time you start Buzhe should be separated 2-3min and then start-up; three times to start Buzhao, should check the reason, can no longer start a row.
3, the winter starts, the engine to heat water, oil should be pre-heating to reduce the load to start the motor and reduce the 8N544 battery output current. In addition, there is no loose wiring clip case, do not force moving wiring chuck in order to avoid a very loose pile.
4, proper maintenance of battery should do the following:
(1), always keep batteries HD438 battery , HF674 batter clean. The outer surface of battery electrolyte spills, dirt, dust, which would cause short-circuit discharge must always wipe clean. Polar head piles and wiring should be kept clean, good contact, and coated with Vaseline to oxidation. Battery lid vent should be kept open in order to avoid gas expansion to enable battery shell rupture.
(2), batteries installed in the locomotive must be fastened securely, and to have anti-vibration pad, so as to avoid driving shattered battery shell. When they find the shell cracking or electrolyte leakage should be timely maintenance.
(3), regularly checked the electrolyte fluid level. Inspection, the application of two openings of the glass tube, insert a finger after a single cell block singalong, and then out observation, is strictly prohibited the use of metal utensils. Surface is insufficient, it is timely to add distilled water; as electrolyte leakage or overflow when the original density of the electrolyte should be added. Add distilled water, it should start the engine to recharge, so that electrolyte mixing.
(4), regularly check the ThinkPad T40 battery deposit of electricity. Application of electrolyte density meter or the discharge fork measurements. When none of these devices can also be speaker volume or the intensity of light to check. Prohibit the use of short-circuit spark discharge to see the size of ways to check to ban the use of tools and objects can be conductive on the battery on the battery off to prevent short circuits.
Second, the immediate lead-acid batteries commonly damage repair
The use of the process, if the battery were damaged, the user can take some temporary measures to repair immediately to an emergency, conditional again when a thorough restoration.
1, very pile ablation, fracture. When the great pile ablation, broken after the repair can be planted wire method. Damage to the very first pile cut from the root level, in its cross-section center drill? 5mm, depth 15mm holes, screw into the M6 × 30 hexagonal screws. The iron pipe on the horn to do a very pile on the molten lead poured into the heated water, after cooling tubes can remove the speaker.
2, shell, cover cracks. If it is found in the vehicle was moving in time, they should first plugging. The side of the battery does not drain the side and wipe away the electrolyte leakage in the ASM 92P1138 battery cover at digging some sealing material, in the exhaust pipe after Hongre Trap. If the slab cracks, the application hacksaw sawing supplemented after the V-groove. For the small cracks, can be used adhesive bonding. Approach is to first crack at local heat until softened after the knife cut into V-shaped crack along a small groove and then with a good resin to be squeezed clay patch Department, Tu Ping, after paper stickers, ready to put its own house sclerosis immediately after use.
3, plate short circuit. Multi-partition is damaged or the bottom of the sediments due to too much lead. Ruoyin partition is damaged, should open the battery, replacing bulkheads. If only a single cell of the partition is damaged, can be removed separately, a single cell of the plate group repairs. Ruoyin too much sediment should be poured electrolyte, cleaned with distilled water after repeated charging.
4, very active material off the board. Active material shed much, they can continue to use after the removal of sediments.
5, plate curing. More than a long-term due to battery discharge in a discharge or semi-state, produces a very thick plate-shaped grains caused by lead sulfate. If curing is not serious, can be used for recharging small current long ways in which the active material recovery, methods of operation are as follows: first by 20h-discharge rate XD736 battery discharge end power, poured out all the electrolyte, washed several times with distilled water and then injected into distilled water to the standard liquid. The second phase of the initial charge with the charge current charge, and to keep measuring the density of electrolyte, when the density increased to 1.15g/cm3 stops charging. Then pour the entire inside of a single electrolyte, and then injected into distilled water and continue to charge. So over and over again, until no longer be increased until the density of the electrolyte. Last to conduct a discharge, and then its fully charged, the electrolyte density can be adjusted to the desired value. The charge to the vulcanization of GW240 battery , its capacity should be restored to the rated capacity of more than 80%. Otherwise, it should be further carried out a number of charge and discharge processing.
6, sealing plastic rupture. If the small cracks that can be used hot iron hot together. If the crack larger, severe electrolyte leakage, should eliminate, re-casting. In order to seal the shell material and a reliable combination of pouring Department should be cleaned with cotton dipped in alkaline to acid.
7, battery circuit. After the Precision M65 battery of a single-cell circuit can be used across the open circuit wires thick enough to single-cell temporary use.
First, the use of lead-acid battery maintenance
1, the correct installation Datie pole piles. The present agricultural vehicles and tractors on the generator with the rectifier is equipped with the battery negative Datie, and DC generator with laptop battery is used in cathode Datie, can not hold against; otherwise the former will burn silicon diode, which will burn regulator contact. Lead-acid battery pole pile marked “+” sign is positive, marked “-” number is negative. No tags, you can identify by the following characteristics: a very thick pile is positive, smaller is the negative; great pile on the oxide is more positive, less is negative; very dark brown pile is positive, pale gray is negative; also available from the poles leads to a pile on each wire, 1K500 battery , 1X793 battery inserted in the same acid in the cup, there are a large number of bubbles produced is negative.
2, do not make excessive battery discharge. Use electric starter starts, each operation shall not exceed 5s; the first time you start Buzhe should be separated 2-3min and then start-up; three times to start Buzhao, should check the reason, can no longer start a row.
3, the winter starts, the engine to heat water, oil should be pre-heating to reduce the load to start the motor and reduce the 8N544 battery output current. In addition, there is no loose wiring clip case, do not force moving wiring chuck in order to avoid a very loose pile.
4, proper maintenance of battery should do the following:
(1), always keep batteries HD438 battery , HF674 batter clean. The outer surface of battery electrolyte spills, dirt, dust, which would cause short-circuit discharge must always wipe clean. Polar head piles and wiring should be kept clean, good contact, and coated with Vaseline to oxidation. Battery lid vent should be kept open in order to avoid gas expansion to enable battery shell rupture.
(2), batteries installed in the locomotive must be fastened securely, and to have anti-vibration pad, so as to avoid driving shattered battery shell. When they find the shell cracking or electrolyte leakage should be timely maintenance.
(3), regularly checked the electrolyte fluid level. Inspection, the application of two openings of the glass tube, insert a finger after a single cell block singalong, and then out observation, is strictly prohibited the use of metal utensils. Surface is insufficient, it is timely to add distilled water; as electrolyte leakage or overflow when the original density of the electrolyte should be added. Add distilled water, it should start the engine to recharge, so that electrolyte mixing.
(4), regularly check the ThinkPad T40 battery deposit of electricity. Application of electrolyte density meter or the discharge fork measurements. When none of these devices can also be speaker volume or the intensity of light to check. Prohibit the use of short-circuit spark discharge to see the size of ways to check to ban the use of tools and objects can be conductive on the battery on the battery off to prevent short circuits.
Second, the immediate lead-acid batteries commonly damage repair
The use of the process, if the battery were damaged, the user can take some temporary measures to repair immediately to an emergency, conditional again when a thorough restoration.
1, very pile ablation, fracture. When the great pile ablation, broken after the repair can be planted wire method. Damage to the very first pile cut from the root level, in its cross-section center drill? 5mm, depth 15mm holes, screw into the M6 × 30 hexagonal screws. The iron pipe on the horn to do a very pile on the molten lead poured into the heated water, after cooling tubes can remove the speaker.
2, shell, cover cracks. If it is found in the vehicle was moving in time, they should first plugging. The side of the battery does not drain the side and wipe away the electrolyte leakage in the ASM 92P1138 battery cover at digging some sealing material, in the exhaust pipe after Hongre Trap. If the slab cracks, the application hacksaw sawing supplemented after the V-groove. For the small cracks, can be used adhesive bonding. Approach is to first crack at local heat until softened after the knife cut into V-shaped crack along a small groove and then with a good resin to be squeezed clay patch Department, Tu Ping, after paper stickers, ready to put its own house sclerosis immediately after use.
3, plate short circuit. Multi-partition is damaged or the bottom of the sediments due to too much lead. Ruoyin partition is damaged, should open the battery, replacing bulkheads. If only a single cell of the partition is damaged, can be removed separately, a single cell of the plate group repairs. Ruoyin too much sediment should be poured electrolyte, cleaned with distilled water after repeated charging.
4, very active material off the board. Active material shed much, they can continue to use after the removal of sediments.
5, plate curing. More than a long-term due to battery discharge in a discharge or semi-state, produces a very thick plate-shaped grains caused by lead sulfate. If curing is not serious, can be used for recharging small current long ways in which the active material recovery, methods of operation are as follows: first by 20h-discharge rate XD736 battery discharge end power, poured out all the electrolyte, washed several times with distilled water and then injected into distilled water to the standard liquid. The second phase of the initial charge with the charge current charge, and to keep measuring the density of electrolyte, when the density increased to 1.15g/cm3 stops charging. Then pour the entire inside of a single electrolyte, and then injected into distilled water and continue to charge. So over and over again, until no longer be increased until the density of the electrolyte. Last to conduct a discharge, and then its fully charged, the electrolyte density can be adjusted to the desired value. The charge to the vulcanization of GW240 battery , its capacity should be restored to the rated capacity of more than 80%. Otherwise, it should be further carried out a number of charge and discharge processing.
6, sealing plastic rupture. If the small cracks that can be used hot iron hot together. If the crack larger, severe electrolyte leakage, should eliminate, re-casting. In order to seal the shell material and a reliable combination of pouring Department should be cleaned with cotton dipped in alkaline to acid.
7, battery circuit. After the Precision M65 battery of a single-cell circuit can be used across the open circuit wires thick enough to single-cell temporary use.